FR 200 Silicone

« Zur Übersicht
FR 200 Silicone
Product description
Zettex FR 200 is a single-part, neutral silicone sealant for fire-resistant sealing. This fire-resistant sealant is specially designed for sealing joints where a fire-resistant layer is essential. Zettex FR 200 adheres excellently to a wide range of porous and non-porous substrates.

Material
Silicones

Advantages
• 4 hours fire-resistance
• No halogen, asbestos or solvents.
• Odourless.
• Neutral fast curing.
• High degree of elasticity.
• Excellent primer-free adhesion for a wide range of construction materials
• Very good resistance to UV, the weather and ageing.
• Long life.
Available forms
• Tube 310 ml
Application instructions
• Fire-resistant expansion joint sealant for construction and glazing applications. For example:
• Prefabricated panels, curtain walls, façades and partition walls.
• Ventilation and flues, cable pipework, pipelines.
• Installation of glass in a fire-resistant wall.
• All applications where fire protection is needed.

The surfaces must be clean, dry and free of grease and dust. Neither may there be any old sealant residues on the surface. Although the FR 200 adheres excellently to most common surfaces it is recommended to first carry out a test. A primer may first be applied for optimal adhesion to some surfaces. Residues that have not properly hardened can be removed with Zettex Profireiniger. Hardened residues can be mechanically removed. It is not advised to use Zettex FR 200 on bituminous surfaces or on building materials on which oil substances are present. No adhesion possible to PE, PP and PTFE. It is advised to first carry out a test on unknown materials. FR 200 cannot be painted over. 
Eigenschaft Spezifikation
Raw material Single-part oxime silicones
Odour Odourless
Consistency Porous
Specific gravity +- 1.25 g/ml
Skin formation time +- 20 minutes (at 23℃; 50 % R.H.)
Curing time +- 2-3 mm after 24 hours (at 23℃; 50 % R.H.)
Temperature for use Between 5℃ and 40 ℃
Shore hardness 25
Movement absorption +- 25 %
Modulus at 100 % stretch 0.38
Tensile strength 1.60 MPa.
Skin formation at 23°C 10 minutes
Temperature resistance -40°C to +150°C
Herunterladen MSDS-Datei Stellen Sie eine Frage